ASTM-Kelas 2A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.27 | Si(%)(%) 0,15-0,35 | Mn(%)(%) 0.5-1.0 | P(%)(%) ≦0.035 | S(%)(%) ≦0,04 | Ni(%)(%) 0.5-1.0 | Cr(%)(%) 0,25-0,45 | Mo(%)(%) 0,55-0,70 | V(%)(%) ≦0,05 | Tegangan Hasil (Mpa)(%) ≧450 | Tegangan Tarik (Mpa)(%) 620-790 | Elongasi (%)(%) ≧16 |
Aplikasi
- Forging Baja Paduan yang Ditempa dan Ditempa untuk Bejana Tekanan
Kode Negara
- ASTM
Jenis Baja
- Class 2A
Jenis Baja Terkait
Jenis Baja | Kode Negara | Lagi | SFVQ2B | CNS | Lagi | SFVQ2B | JIS | Lagi | Class 2A | ASTM | Lagi | SFVQ2A | CNS | Lagi | SFVQ2A | JIS | Lagi |
---|