ASTM-Kelas 3A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Cu(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.45 | Si(%)(%) 0,15-0,35 | Mn(%)(%) 0.4-0.9 | P(%)(%) ≦0,04 | S(%)(%) ≦0,04 | Ni(%)(%) 1.0-1.3 | Cr(%)(%) ≦1.5 | Mo(%)(%) ≧0.15 | V(%)(%) ≦0,1 | Cu(%)(%) ≦0.35 | Tebal (mm)(%) ≦254 | Tegangan Hasil (Mpa)(%) ≧550 | Tegangan Tarik (Mpa)(%) ≧725 | Elongasi (%)(%) ≧19 |
Aplikasi
- Forging Baja Nikel Kromium Molibdenum untuk Penggunaan Umum
Kode Negara
- ASTM
Standar
- A291
Jenis Baja
- Class 3A
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | SFNCM75 | 4043 | CNS | Lagi | SFNCM-740 | G3222 | JIS | Lagi | Class 3A | A291 | ASTM | Lagi |
---|