ASTM-F11 Kelas 2
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.1-0.2 | Si(%)(%) 0.5-1.0 | Mn(%)(%) 0.3-0.8 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Cr(%)(%) 1.0-1.5 | Mo(%)(%) 0.44-0.65 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) ≧485 | Elongasi (%)(%) ≧20 |
Aplikasi
- Paduan Baja Forging untuk Bejana Tekanan untuk Layanan Suhu Tinggi