ASTM-F22
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.05-0.15 | Si(%)(%) ≦0.5 | Mn(%)(%) 0.3-0.6 | P(%)(%) ≦0.025 | S(%)(%) ≦0.025 | Cr(%)(%) 2.0-2.5 | Mo(%)(%) 0.90-1.13 | Tegangan Luluh (Mpa)(%) ≧310 | Tegangan Tarik (Mpa)(%) 515-690 | Pemanjangan (%)(%) ≧19 |
Aplikasi
- Paduan Baja Forging untuk Bejana Tekanan untuk Layanan Suhu Tinggi
Kode Negara
- ASTM
Tipe Baja
- F22
Tipe Baja Terkait