ASTM-F321H
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Ti(%) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.04-0.10 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 9.0-12.0 | Cr(%)(%) ≧17.0 | Ti(%)(%) 4xC%-0.7 | Tegangan Luluh (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧515 | Pemanjangan (%)(%) ≧30 |
Aplikasi
- Flens/Fitting/Valve Stainless Steel yang Ditempa dan Bagian dari Bejana Tekanan untuk Tinggi
Kode Negara
- ASTM
Standar
- A182
Tipe Baja
- F321H
Tipe Baja Terkait
| Tipe Baja | Standar | Kode Negara | Lagi | F321H | 8702 | CNS | Lagi | SUSF321H | G3214 | JIS | Lagi | F321H | A336 | ASTM | Lagi | X6CrNi-Til8-10 | 17440 | DIN | Lagi | F321H | A182 | ASTM | Lagi |
|---|