ASTM-F5
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0.15 | Si(%)(%) ≦0.5 | Mn(%)(%) 0.3-0.6 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.5 | Cr(%)(%) 4.0-6.0 | Mo(%)(%) 0.45-0.65 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) ≧485 | Elongasi (%)(%) ≧20 |
Aplikasi
- Paduan Baja Forging untuk Bejana Tekanan untuk Layanan Suhu Tinggi
Kode Negara
- ASTM
Jenis Baja
- F5
Jenis Baja Terkait