ASTM-F6
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0,12 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.025 | S(%)(%) ≦0.025 | Ni(%)(%) ≦0.5 | Cr(%)(%) 11.5-13.5 | Tegangan Luluh (Mpa)(%) ≧380 | Tegangan Tarik (Mpa)(%) 585-760 | Pemanjangan (%)(%) ≧35 |
Aplikasi
- Flens/Fitting/Valve Stainless Steel yang Ditempa dan Bagian dari Bejana Tekanan untuk Tinggi
Kode Negara
- ASTM
Standar
- A336
Tipe Baja
- F6
Tipe Baja Terkait
| Tipe Baja | Standar | Kode Negara | Lagi | F6A | A182 | ASTM | Lagi | F6 | A336 | ASTM | Lagi | SUSF410 | G3214 | JIS | Lagi | SUSF410B | G3214 | JIS | Lagi | SUSF410C | G3214 | JIS | Lagi | SUSF410D | G3214 | JIS | Lagi |
|---|