ASTM-Gr.A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | V(%) | Cu(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.19 | Si(%)(%) 0.30-0.65 | Mn(%)(%) 0.80-1.25 | P(%)(%) ≦0,04 | S(%)(%) ≦0,05 | Ni(%)(%) ≦0,40 | Cr(%)(%) 0,40-0,65 | V(%)(%) 0.02-0.10 | Cu(%)(%) 0.25-0.40 | Tebal (mm)(%) ≦100 | Tegangan Hasil (Mpa)(%) ≧345 | Tegangan Tarik (Mpa)(%) ≧485 | Elongasi (%)(%) ≧21 |
Aplikasi
- Baja Tahan Korosi Atmosfer Panas Digulung untuk Struktur Las
Kode Negara
- ASTM
Standar
- A588M
Jenis Baja
- Gr.A
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | SMA400AP | 4269 | CNS | Lagi | SMA400AP | G3114 | JIS | Lagi | Gr.A | A588M | ASTM | Lagi |
---|