ASTM-LCC
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Cu(%) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0.25 | Si(%)(%) ≦0.6 | Mn(%)(%) ≦1.2 | P(%)(%) ≦0.04 | S(%)(%) ≦0.045 | Ni(%)(%) ≦0.5 | Cr(%)(%) ≦0.5 | Mo(%)(%) ≦0.2 | V(%)(%) ≦0.03 | Cu(%)(%) ≦0.03 | Tegangan Luluh (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) 485-655 | Pemanjangan (%)(%) ≧22 |