ASTM-Tipe B Kelas 1
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Mo(%) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0.25 | Si(%)(%) 0.15-0.40 | Mn(%)(%) 1.15-1.50 | P(%)(%) ≦0.035 | S(%)(%) ≦0.04 | Ni(%)(%) 0.4-0.7 | Mo(%)(%) 0.45-0.60 | Tegangan Luluh (Mpa)(%) ≧345 | Tegangan Tarik (Mpa)(%) 550-690 | Pemanjangan (%)(%) ≧18 |
Aplikasi
- Pelat Baja Paduan Mn-Mo dan Mn-Mo-Ni yang Dikuatkan dan Ditemper untuk Wadah Tekanan
- Pelat Baja untuk Bejana Tekanan
Kode Negara
- ASTM
Standar
- A533
Tipe Baja
- Type B Class 1
Tipe Baja Terkait
| Tipe Baja | Standar | Kode Negara | Lagi | SQV2A | 8973 | CNS | Lagi | SQV2A | G3120 | JIS | Lagi | Type B Class 1 | A533 | ASTM | Lagi | 20MnMoNi55 | SEW-640 | DIN | Lagi | SPV450 | 4271 | CNS | Lagi | SPV450 | G3115 | JIS | Lagi | Type A Class 1 | A533 | ASTM | Lagi | Type C Class 1 | A533 | ASTM | Lagi |
|---|