| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.25-0.32 | Si(%)(%) ≦0.4 | Mn(%)(%) 1.30-1.65 | P(%)(%) ≦0.035 | S(%)(%) ≦0.035 | Ni(%)(%) ≦0.4 | Cr(%)(%) ≦0.4 | Mo(%)(%) ≦0.1 | Tegangan Hasil (Mpa)(%) ≧440 | Tegangan Tarik (Mpa)(%) 640-790 | Elongasi (%)(%) ≧16 |
Aplikasi
- Paduan Baja Karbon dengan Kekuatan Tarik Tinggi dan Paduan Baja Low Alloy untuk Struktur
Kode Negara
- DIN
Standar
- 1681
Jenis Baja
- 28Mn6