C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | V(%) | Cu(%) | Al(%) | Ti(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.16 | Si(%)(%) ≦0.35 | Mn(%)(%) 0,40-1,20 | P(%)(%) ≦0.035 | S(%)(%) ≦0.035 | Ni(%)(%) ≦0,30 | Cr(%)(%) ≦0.25 | V(%)(%) ≦0.03 | Cu(%)(%) ≦0.03 | Al(%)(%) ≦0.02 | Ti(%)(%) ≦0.03 | Tebal (mm)(%) ≦16 | Tegangan Hasil (Mpa)(%) ≧235 | Tegangan Tarik (Mpa)(%) 350-470 |
Aplikasi
- Pelat Baja Karbon dan Baja Paduan Molibdenum untuk Boiler dan Tangki Tekanan Lainnya