DIN-X5CrNi-18-10
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0.07 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.045 | S(%)(%) ≦0.015 | Ni(%)(%) 11.0-13.0 | Cr(%)(%) 17.0-19.0 | Tegangan Hasil (Mpa)(%) ≧185 | Tegangan Tarik (Mpa)(%) 500-700 | Elongasi (%)(%) ≧50 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- DIN
Standar
- 17440
Jenis Baja
- X5CrNi-18-10
Jenis Baja Terkait
| Jenis Baja | Standar | Kode Negara | Lagi |
F304 |
8702 | CNS | Lagi |
SUSF304 |
G3214 | JIS | Lagi |
F304 |
A182 | ASTM | Lagi |
F304 |
A336 | ASTM | Lagi |
X5CrNi-18-10 |
17440 | DIN | Lagi |
|---|