JIS-SCC3A
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|
| C(%)(%) 0.3-0.4 | Si(%)(%) 0.3-0.6 | Mn(%)(%) 0.5-0.8 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Tegangan Luluh (Mpa)(%) ≧265 | Tegangan Tarik (Mpa)(%) ≧520 | Pemanjangan (%)(%) ≧13 |
Aplikasi
- Paduan Baja Karbon Kekuatan Tarik Tinggi dan Paduan Baja Rendah untuk Struktur
Kode Negara
- JIS
Standar
- G5111
Tipe Baja
- SCC3A
Tipe Baja Terkait
| Tipe Baja | Standar | Kode Negara | Lagi | SCC3A | 7145 | CNS | Lagi | SCC3A | G5111 | JIS | Lagi | 80-40 | A148 | ASTM | Lagi | GS-60 | 1681 | DIN | Lagi |
|---|