JIS-SCCrM3B
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.3-0.4 | Si(%)(%) 0.3-0.6 | Mn(%)(%) 0.5-0.8 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Cr(%)(%) 0.8-1.2 | Mo(%)(%) 0.15-0.35 | Tegangan Luluh (Mpa)(%) ≧540 | Tegangan Tarik (Mpa)(%) ≧740 | Pemanjangan (%)(%) ≧9 |
Aplikasi
- Paduan Baja Karbon Kekuatan Tarik Tinggi dan Paduan Baja Rendah untuk Struktur
Kode Negara
- JIS
Standar
- G5111
Tipe Baja
- SCCrM3B
Tipe Baja Terkait
| Tipe Baja | Standar | Kode Negara | Lagi |
SCCrM3B |
7145 | CNS | Lagi |
SCCrM3B |
G5111 | JIS | Lagi |
105-85 |
A148 | ASTM | Lagi |
|---|