ASTM-CA-40
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Streckgrenze (Mpa) | Zugfestigkeit (Mpa) | Dehnung (%) |
|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.2-0.4 | Si(%)(%) ≦1.5 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni(%)(%) ≦1.0 | Cr(%)(%) 11,5-14,0 | Mo(%)(%) ≦0,5 | Streckgrenze (Mpa)(%) ≧485 | Zugfestigkeit (Mpa)(%) ≧690 | Dehnung (%)(%) ≧15 |
Anwendungen
- Edelstahlgussstücke
Ländercode
- ASTM
Standard
- A743
Stahltyp
- CA-40