ASTM-LF2
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Cu(%) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0.3 | Si(%)(%) 0.15-0.30 | Mn(%)(%) 0.60-1.35 | P(%)(%) ≦0.035 | S(%)(%) ≦0.04 | Ni(%)(%) ≦0.4 | Cr(%)(%) ≦0.3 | Mo(%)(%) ≦0,12 | V(%)(%) ≦0.03 | Cu(%)(%) ≦0.4 | Tegangan Luluh (Mpa)(%) ≧250 | Tegangan Tarik (Mpa)(%) 485-655 | Pemanjangan (%)(%) ≧22 |
Aplikasi
- Paduan Baja dan Baja Karbon untuk Pengecoran Tekanan untuk Layanan Suhu Rendah
Lainnya
- Nb : ≦0.02
Kode Negara
- ASTM
Standar
- A350
Tipe Baja
- LF2
Tipe Baja Terkait