DIN-TStE 315
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Cu(%) | Al(%) | N(%) | Tebal (mm) | Tegangan Luluh (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0,16 | Si(%)(%) ≦0.45 | Mn(%)(%) 0,7-1,5 | P(%)(%) ≦0.03 | S(%)(%) ≦0.025 | Ni(%)(%) ≦0.3 | Cr(%)(%) ≦0.3 | Mo(%)(%) ≦0.08 | Cu(%)(%) ≦0.3 | Al(%)(%) ≧0.02 | N(%)(%) ≦0.02 | Tebal (mm)(%) 60≦t≦70 | Tegangan Luluh (Mpa)(%) ≧295 | Tegangan Tarik (Mpa)(%) 440-560 | Pemanjangan (%)(%) ≧23 |
Aplikasi
- Paduan Baja dan Baja Karbon untuk Pengecoran Tekanan untuk Layanan Suhu Rendah
Lainnya
- Nb : ≦0.03
Kode Negara
- DIN
Tipe Baja
- TStE 315
Tipe Baja Terkait
| Tipe Baja | Standar | Kode Negara | Lagi | TStE 315 | DIN | Lagi | SFL2 | 11067 | CNS | Lagi | SFL2 | G3205 | JIS | Lagi | LF2 | A350 | ASTM | Lagi |
|---|