ASTM-F1
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.2-0.3 | Si(%)(%) 0.20-0.35 | Mn(%)(%) 0.6-0.9 | P(%)(%) ≦0.025 | S(%)(%) ≦0.025 | Mo(%)(%) 0.40-0.66 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) 485-660 | Pemanjangan (%)(%) ≧20 |
Aplikasi
- Paduan Keluli Ditempa untuk Bekas Tekanan untuk Perkhidmatan Suhu Tinggi
- Keluli Alat Aloi(1)
Kod Negara
- ASTM
Jenis Baja
- F1
Hubungi Jenis Baja