JIS-SCH19
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.2-0.5 | Si(%)(%) ≦2.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni(%)(%) 23.0-27.0 | Cr(%)(%) 19.0-23.0 | Mo(%)(%) ≦0.5 | Tegangan Tarik (Mpa)(%) ≧390 | Pemanjangan (%)(%) ≧5 |
Aplikasi
- Tuangan Keluli Tahan Panas
Kod Negara
- JIS
Standard
- G5122
Jenis Baja
- SCH19
Jenis Baja yang Berkaitan
| Jenis Baja | Standard | Kod Negara | More |
SCH19 |
4002 | CNS | More |
ZG35Ni24-Cr18Si2 |
8492 | GB | More |
SCH19 |
G5122 | JIS | More |
HN |
A297 | ASTM | More |
|---|