JIS-SCS14A
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0.08 | Si(%)(%) ≦1.5 | Mn(%)(%) ≦1.5 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni(%)(%) 9.0-12.0 | Cr(%)(%) 18.0-21.0 | Mo(%)(%) 2.0-3.0 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧480 | Pemanjangan (%)(%) ≧33 |
Aplikasi
- Tuangan Keluli Tahan Karat
Kod Negara
- JIS
Standard
- G5121
Jenis Baja
- SCS14A
Jenis Baja yang Berkaitan
| Jenis Baja | Standard | Kod Negara | More |
SCS14A |
4000 | CNS | More |
ZG0Cr18Ni-12Mo2Ti |
2100 | GB | More |
SCS14A |
G5121 | JIS | More |
CF-8M |
A351 | ASTM | More |
CF-8M |
A743 A744 | ASTM | More |
G-X6CrNi-Mo18-10 |
17445 | DIN | More |
|---|