JIS-SFVA-F11A
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) ≦0.2 | Si(%)(%) 0.5-1.0 | Mn(%)(%) 0.3-0.8 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Cr(%)(%) 1.0-1.5 | Mo(%)(%) 0.45-0.65 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) 480-660 | Pemanjangan (%)(%) ≧18 |
Aplikasi
- Paduan Keluli Forging untuk Bekas Tekanan untuk Perkhidmatan Suhu Tinggi
Kod Negara
- JIS
Jenis Baja
- SFVA-F11A
Jenis Baja yang Berkaitan
| Inquiry | Jenis Baja | Kod Negara | More |
SFVA-F11A |
CNS | More |
15CrMo |
GB | More |
SFVA-F11A |
JIS | More |
F11 Class 2 |
ASTM | More |
F11 |
ASTM | More |
13CrMo-4-4 |
DIN | More |
|---|