CNS-SCH22
| C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
|---|---|---|---|---|---|---|---|---|---|---|
| C(%)(%) 0.35-0.45 | Si(%)(%) ≦1.75 | Mn(%)(%) ≦1.5 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni(%)(%) 19.0-22.0 | Cr(%)(%) 23.0-27.0 | Mo(%)(%) ≦0.5 | Tegangan Hasil (Mpa)(%) ≧235 | Tegangan Tarik (Mpa)(%) ≧440 | Pemanjangan (%)(%) ≧8 |
Aplikasi
- Tuangan Keluli Tahan Panas
Kod Negara
- CNS
Standard
- 4002
Jenis Baja
- SCH22
Jenis Baja yang Berkaitan
| Jenis Baja | Standard | Kod Negara | More |
SCH22 |
4002 | CNS | More |
ZG40Cr25-Ni20 |
8492 | GB | More |
SCH22 |
G5122 | JIS | More |
HK40 |
A351 | ASTM | More |
G-X40Cr-NiSi25-20 |
17465 | DIN | More |
|---|